Datasheet - Rod/wire electrode for Copper alloys

Typical composition in %  
Al 8,50 - 9,50
Si < 0,10
Mn 0,60 - 3,50
Ni incl. Co 4,00 - 5,50
Zn < 0,10
Pb < 0,02
Fe 3,00 - 5,00
Others total < 0,50
Classification  
ISO 24373 S Cu 6328 (CuAl9Ni5Fe3Mn2)
DIN 1733 SG-CuAl8Ni6
Material No. 2.0923
BS 2901 part 3 C 26 Ni
AWS A 5.7 ER CuNiAl
Base materials
CuAl11Ni6Fe5; CuAl10Ni5Fe4; Copper-Aluminium-Nickel alloys in general
Remarks

Filler metal for Cu-Al-Ni-materials and for castings and forged parts from Nickel-Aluminium bronzes. Surfacing of Al-bronzes and aluminium coated steels, and complex bronzes. Excellent sea water restistance (i.e. surfacing of ship's propellors). High wear and abrasion resistance. Suitable for bearings, valves, turbines, pumps etc.

Physical properties (Approx. values)  
Electrical conductivity [S*m/mm²] 4
Density [kg/dm³] 7,5
Solidus-Temperature [° C] 1015
Liquidus-Temperature [° C] 1045
Tensile strength Rm [MPa] 450 - 560
Elongation A5 (Lo=5d0) [%] 10
Hardness [HB] 150 - 170
Svetspositioner
PA, PB, PC, PD, PE, PF
PA
PA
PB
PC
PC
PD
PE
PE
PF
PF
Skyddsgas
I1, I2, I3 (argon, helium eller argon/helium blandningar
Polarity
MIG =+
Dimensions  
MIG-wires [mm] 1,0; 1,2; 1,6;
Packaging
Spools Packaging units
B 300 / BS 300 / 15 kg 25 spools = 375 kg (Pallet)
B-300 15 kg
B-300 15 kg
BS-300 15 kg
BS-300 15 kg
B-300, BS-300, S-300 box

MIG wires

DesignationItem numberQuantity in
stock [kg]
Wire electrode CuAl8Ni6 D=1,0mm 8,0923,03,100
Wire electrode CuAl8Ni6 D=1,2mm 8,0923,03,120